مادة أسلاك الفولاذ المقاوم للصدأ
يسرد الجدول أدناه مواد الأسلاك بناءً على الدرجات.
ASTM/ASME
Grade |
EN Grade |
GB Unified
Number |
Chemical Component % |
C |
Cr |
Ni |
Mn |
P |
S |
Mo |
Si |
Cu |
N |
Other |
201 |
1.4372 |
1Cr17Mn6Ni5N |
≤0.15 |
16.00-18.00 |
3.50-5.50 |
5.50-7.50 |
≤0.060 |
≤0.030 |
– |
≤1.00 |
– |
≤0.25 |
– |
202 |
1.4373 |
1Cr18Mn8Ni5N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
7.50-10.00 |
≤0.060 |
≤0.030 |
|
≤1.00 |
– |
≤0.25 |
- |
301 |
1.4310 |
1Cr17Ni7 |
≤0.15 |
16.00-18.00 |
6.00-8.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤1.00 |
– |
0.1 |
– |
302 |
1.4325 |
1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.035 |
≤0.030 |
– |
≤1.00 |
– |
– |
– |
303 |
1.4305 |
Y1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.20 |
≥0.15 |
– |
≤1.00 |
– |
– |
– |
304 |
1.4301 |
0Cr18Ni9 |
≤0.08 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤0.75 |
– |
– |
– |
304L |
1.4307 |
00Cr19Ni10 |
≤0.030 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤0.75 |
– |
– |
– |
304H |
1.4948 |
0Cr18Ni9 |
0.04~0.10 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤0.75 |
– |
– |
– |
309S |
1.4833 |
0Cr23Ni13 |
≤0.08 |
22.00-24.00 |
12.00-15.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤0.75 |
– |
– |
– |
309 |
1.4828 |
0Cr23Ni13 |
0.04~0.10 |
22.00-24.00 |
12.00-15.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤0.75 |
– |
– |
– |
310S |
1.4842 |
0Cr25Ni20 |
≤0.08 |
24.00-26.00 |
19.00-22.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤1.5 |
– |
– |
– |
310H |
1.4821 |
0Cr25Ni20 |
0.04~0.10 |
24.00-26.00 |
19.00-22.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤1.5 |
– |
– |
– |
314 |
1.4841 |
0Cr25Ni20Si |
≤0.25 |
23.00-26.00 |
19.00-22.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
1.5-3.0 |
– |
– |
– |
316 |
1.4401 |
0Cr17Ni12Mo2 |
≤0.08 |
16.00-18.50 |
10.00-14.00 |
≤2.00 |
≤0.045 |
≤0.030 |
2.00-3.00 |
≤0.75 |
– |
– |
– |
316L |
1.4404 |
00Cr17Ni14Mo2 |
≤0.030 |
16.00-18.00 |
10.00-14.00 |
≤2.00 |
≤0.045 |
≤0.030 |
2.00-3.00 |
≤0.75 |
– |
– |
– |
316H |
1.4436 |
0Cr17Ni12Mo2N |
0.04~0.10 |
16.00-18.00 |
10.00-14.00 |
≤2.00 |
≤0.045 |
≤0.030 |
2.00-3.00 |
≤0.75 |
– |
0.10-0.22 |
– |
316Ti |
1.4571 |
0Cr17Ni12Mo2Ti |
≤0.08 |
16.00-18.50 |
10.00-14.00 |
≤2.00 |
≤0.045 |
≤0.030 |
2.00-3.00 |
≤0.75 |
– |
– |
Ti5(C+N)~0.7 |
317 |
1.4445 |
0Cr19Ni13Mo3 |
≤0.08 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
≤0.045 |
≤0.030 |
3.00-4.00 |
≤0.75 |
– |
0.1 |
– |
317L |
1.4438 |
00Cr19Ni13Mo3 |
≤0.03 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
≤0.045 |
≤0.030 |
3.00-4.00 |
≤0.75 |
– |
0.1 |
– |
321 |
1.4541 |
0Cr18Ni10Ti |
≤0.08 |
17.00-19.00 |
9.00-12.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤0.75 |
– |
0.1 |
Ti5(C+N)~0.7 |
321H |
1.4940 |
0Cr18Ni10Ti |
0.04~0.10 |
17.00-19.00 |
9.00-12.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤0.75 |
– |
0.1 |
Ti4(C+N)~0.7 |
329 |
1.4480 |
0Cr26Ni5Mo2 |
≤0.08 |
23.00-28.00 |
2.00-5.00 |
≤1.00 |
≤0.040 |
≤0.030 |
1.00-2.00 |
≤0.75 |
– |
– |
– |
329J1 |
1.4480 |
0Cr26Ni5Mo2 |
≤0.08 |
23.00-28.00 |
2.00-5.00 |
≤1.00 |
≤0.045 |
≤0.030 |
1.00-2.00 |
≤0.75 |
– |
– |
– |
330 |
1.4864 |
N08330 |
≤0.15 |
14.00-17.00 |
33.00-37.00 |
≤2.00 |
≤0.045 |
≤0.040 |
1.00-2.00 |
≤1.5 |
– |
– |
– |
347 |
1.4550 |
0Cr18Ni11Nb |
≤0.08 |
17.00-19.00 |
9.00-13.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤0.75 |
– |
– |
Nb≥10*C%-1.0 |
347H |
1.4912 |
0Cr18Ni11Nb |
0.04~0.10 |
17.00-19.00 |
9.00-13.00 |
≤2.00 |
≤0.045 |
≤0.030 |
– |
≤0.75 |
– |
– |
Nb≥8*C%-1.0 |
409L |
1.4720 |
S40900 |
≤0.03 |
10.50-11.70 |
0.5 |
≤1.00 |
≤0.040 |
≤0.020 |
– |
≤1.00 |
– |
0.03 |
Ti6(C+N)-0.5 Nb0.17 |
430 |
1.4016 |
S43000 |
≤0.12 |
16.00-18.00 |
0.75 |
≤1.00 |
≤0.040 |
≤0.030 |
– |
≤1.00 |
– |
– |
– |
436 |
1.4513 |
S43600 |
≤0.025 |
16.00-19.00 |
– |
≤1.00 |
≤0.040 |
≤0.030 |
0.75-1.0 |
≤1.00 |
|
≤0.025 |
Nb+Ti:8(C+N)~0.80 |
439 |
1.4510 |
S43035 |
≤0.030 |
17.50-18.50 |
– |
≤1.00 |
≤0.040 |
≤0.015 |
– |
≤1.00 |
– |
≤0.030 |
Ti+Nb:0.2+4C~0.75 |
441 |
1.4509 |
S44100 |
≤0.030 |
17.50-18.50 |
– |
≤1.00 |
≤0.040 |
≤0.015 |
– |
≤1.00 |
– |
≤0.030 |
Ti:0.1-0.6 Nb:3C+0.3~1.0 |
442 |
1.4741 |
S44200 |
≤0.025 |
18.0-23.0 |
– |
≤1.00 |
≤0.040 |
≤0.035 |
– |
≤1.00 |
– |
|
|
443 |
|
S44300 |
≤0.025 |
19.5-22.0 |
– |
≤1.00 |
≤0.035 |
≤0.015 |
– |
≤1.00 |
– |
≤0.025 |
Nb+Ti:0.2+4(C+N)~0.75 |
444 |
1.4521 |
S44400 |
≤0.025 |
17.00-20.00 |
– |
≤1.00 |
≤0.040 |
≤0.030 |
1.75-2.5 |
≤1.00 |
|
≤0.035 |
Ti+Nb:0.2+4(C+N)~0.8 |
446 |
1.4749 |
S44600 |
≤0.2 |
23.0-27.0 |
0.75 |
≤1.50 |
≤0.040 |
≤0.030 |
– |
≤1.00 |
|
0.25 |
|
410 |
1.4006 |
1Cr13 |
0.08~0.15 |
11.50-13.50 |
– |
≤1.00 |
≤0.040 |
≤0.030 |
– |
≤1.00 |
– |
– |
– |
420 |
1.4031 |
2Cr13 |
≥0.15 |
12.00-14.00 |
– |
≤1.00 |
≤0.040 |
≤0.030 |
– |
≤1.00 |
– |
– |
– |
420J2 |
1.4028 |
3Cr13 |
0.26-0.35 |
12.00-14.00 |
– |
≤1.00 |
≤0.040 |
≤0.030 |
– |
≤1.00 |
– |
– |
– |
S42040 |
1.4034 |
4Cr13 |
0.36-0.45 |
12.00-14.00 |
– |
≤1.00 |
≤0.040 |
≤0.030 |
– |
≤1.00 |
– |
– |
– |
431 |
1.4057 |
1Cr17Ni2 |
≤0.2 |
15.00-17.00 |
1.25-2.50 |
≤1.00 |
≤0.040 |
≤0.030 |
– |
≤1.00 |
– |
– |
– |
440A |
1.4040 |
7Cr17 |
0.60-0.75 |
16.00-18.00 |
– |
≤1.00 |
≤0.040 |
≤0.030 |
0.75 |
≤1.00 |
– |
– |
– |
440B |
1.4041 |
8Cr17 |
0.75-0.95 |
16.00-18.00 |
– |
≤1.00 |
≤0.040 |
≤0.030 |
0.75 |
≤1.00 |
– |
– |
– |
440C |
1.4023 |
11Cr17 |
0.95-1.20 |
16.00-18.00 |
– |
≤1.00 |
≤0.040 |
≤0.030 |
0.75 |
≤1.00 |
– |
– |
– |
17-4PH |
1.4542 |
630 |
≤0.07 |
15.50-17.50 |
3.00-5.00 |
≤1.00 |
≤0.040 |
≤0.030 |
– |
≤1.00 |
3.00-5.00 |
– |
Nb+Ta:0.15-0.45 |
17-7PH |
1.4568 |
631 |
≤0.09 |
16.00-18.00 |
6.50-7.50 |
≤1.00 |
≤0.040 |
≤0.030 |
– |
≤1.00 |
– |
– |
Al 0.75-1.50 |
15-5PH |
1.4545 |
S15500 |
≤0.09 |
14.00-15.50 |
3.50-5.50 |
≤1.00 |
≤0.040 |
≤0.030 |
2.00-3.00 |
≤1.00 |
2.50-4.50 |
– |
|
416 |
1.4005 |
Y1Cr13 |
≤0.15 |
12.00-14.00 |
– |
≤1.25 |
≤0.06 |
≥0.15 |
– |
≤1.00 |
– |
– |
– |
420F |
1.4029 |
Y3Cr13 |
0.3-0.40 |
12.00-14.00 |
0.5 |
≤1.25 |
≤0.06 |
≥0.15 |
– |
≤1.00 |
0.6 |
– |
– |
430F |
1.4019,1.4104 |
Y1Cr17 |
≤0.12 |
16.00-18.00 |
– |
≤1.25 |
≤0.06 |
≥0.15 |
– |
≤1.00 |
– |
– |
– |
440F |
1.4025 |
Y11Cr17 |
0.95-1.20 |
16.00-18.00 |
– |
≤1.25 |
≤0.06 |
≥0.15 |
– |
≤1.00 |
– |
– |
– |
303 |
1.4305 |
S30317 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.20 |
≥0.15 |
– |
≤1.00 |
– |
– |
– |